HUS-Double Wall Heat Shrinkable Tube


Product Overview:

HUS-Double Wall Heat Shrinkable Tube ( Inner layer with the EVA adhesive or PA Glue, also called Adhesive shrinkalbe tube ) ,  Outer layers made of flame-resistant insulation materials of polyolefin PE and EVA hot-melt Adhesive transparent double form, Environmental protection double wall heat shrink tube often applicable to all types of wire harnesses, wire and cable, wire, connectors, metal tubes need to be waterproof, moisture-proof, anticorrosive insulation sealing, bundling fixed and other areas of the environment.
Contact us
  • Product Features
  • Specifications
  • Technical data
  • Video
  • Adhesive lined heat shrink tubing with environmental sealing capability for a wide variety of electrical applications, including automotive and marine wire harness, wire splices, breakouts, and connector-to-cable transitions.


    Product features:

     1, Flame-resistant, anti-UV

     2, Heat Shrink Ratio:  3:1  ,  4:1

     3, waterproof, damp-proof, anti-corrosion, prevent gas leakage.

     4, RoHs2.0,  REACH,

     

    Operation indicator:
    Shrink temperature:70℃
    End temperature:125℃
    Working temperature:-45℃~125℃


    Conformance to standard:Approvals
    Comply with UL224 ,125℃, 600V 

    Key words:
    • Glue heat shrinkable tubing
    • Adhesive heat shrinkable tube
    • Waterproof heat shrink tubing
  • Nominal Size As supplied (mm) After recovered   ( mm ) Standard Packing
    (M/Roll)
    (Inch mm D :Inside
    diameter
    :Inside diameter T: Total wall  thickness t. Adhesivel thickness
    HUS-3X3:1
    3/32 Φ2.4 ≥2.4 ≤0.80 0.80±0.30  0.40±0.20 200
    1/8 φ3.2 ≥3.2 ≤1.00 0.90±0.30  0.40±0.20 200
    3/16 φ4.8 ≥4.8 ≤1.60 1.05±0.30  0.40±0.20 100
    1/4 φ6.4 ≥6.4 ≤2.20 1.25±0.30   0.45±0.20 100
    5/16 φ7.9 ≥7.9 ≤2.70 1.35±0.30   0.45±0.20 100
    3/8 φ9.5 ≥9.5 ≤3.20 1.45±0.30 0.50±0.20 50
    1/2 φ12.7 ≥12.7 ≤4.20 1.65±0.30 0.50±0.20 1.22
    5/8 φ15.0 ≥15.0 ≤5.20 1.80±0.30 0.55±0.30 1.22
    3/4 φ19.1 ≥19.1 ≤6.30 1.95±0.30 0.60±0.30 1.22
    1 φ25.4 ≥25.4 ≤8.50 2.00±0.40 0.60±0.30 1.22
    1-1/4 φ30.0 ≥30.0 ≤10.20 2.15±0.40 0.65±0.30 1.22
    1-1/2 φ39.0 ≥39.0 ≤13.50 2.45±0.40 0.75±0.30 1.22
    2 φ50.0 ≥50.0 ≤17.00 2.75±0.40 0.80±0.30 1.22
    2-1/2 Φ64.0 ≥64.0 ≤21.00 3.05±0.40 1.05±0.30 1.22
    3 Φ75.0 ≥75.0 ≤25.00 3.05±0.50 1.05±0.40 1.22
    3-1/2 Φ90.0 ≥90.0 ≤30.00 3.10±0.50 1.05±0.40 1.22
    4 Φ100 ≥100 ≤34.00 3.10±0.50 1.10±0.40 1.22
    5 Φ125 ≥125 ≤42.00 3.15±0.50 1.10±0.40 1.22
    HUS-4X
    2/13 Φ4.0 ≥4.0 ≤1.0 1.05±0.30 0.50±0.30 200
    1/4 Φ6.0 ≥6.0 ≤1.5 1.15±0.30 0.50±0.30 100
    5/16 Φ8.0 ≥8.0 ≤2.0 1.15±0.30 0.60±0.30 100
    1/2 Φ12.0 ≥12.0 ≤3.0 1.75±0.30 0.60±0.30 1.22
    5/8 Φ16.0 ≥16.0 ≤4.0 2.00±0.30 0.70±0.30 1.22
    15/19 Φ20.0 ≥20.0 ≤5.0 2.30±0.40 0.70±0.30 1.22
    1 Φ24.0 ≥24.0 ≤6.0 2.60±0.40 0.75±0.30 1.22
    1-1/4 Φ32.0 ≥32.0 ≤8.0 3.00±0.50 0.90±0.30 1.22
    2 Φ52.0 ≥52.0 ≤13.0 3.35±0.50 0.95±0.30 1.22
  • Product Property Test method Test Date
    Tensile strength ASTM D 2671 10.4MPa
    Elongation at break ASTM D 2671 200
    Tensile strength after aging 158,168hrs 7.3MPa
    Elongation at Break
     after aging%
    100
    Longitudinal shrinkage ASTM D 2671 -8%+8%
    Dielectric strengthkv/mm IEC 60243 15KV/mm
    Flammability ASTM D 2671B 通过
    Volume resistance IEC 60093 1014Ωcm(min.)
    Hot melt adhesive technology index
     water absorption < 0.2% ASTM-D570
    Vicat Softening Point 95 ASTM-E28
    peel strength (PE) 120N/25mm ASTM D 1000
    peel strength (AI) 80N/25mm ASTM D 1000
    MaterialPE  +  hot-melt adhesive