• Product name: KY-CX magnetic heat shrinkable sleeving

Product introduction:
Magnetic heat-shrinkable sleeve is made of high quality polymers, scientific formula, mechanical blending of polymer alloys, after forming the electron Accelerator irradiation cross-linking and continuous expansion. Products not only with conventional heat-shrinkable sleeve protection, insulation, identifying properties and good electromagnetic compatibility, can greatly improve the electronic components and magnetic properties and stability. Low cost, stable performance, simple installation, contract evenly, can be widely used in the electronic components industry.

Operation indicator
1、Applicable temperature range:-55℃— 125℃; 
2、Shrink temperature:100℃—125℃;
Conformance to standard:Approvals
Conform width ROHS

Size
(mm)
As supplied (mm) After recovered(mm)  Standard Packing
(M/Roll) 
Application(mm)
Inside diameter Wall thickness Inside diameter Wall thickness
Φ4.0 4.5±0.4 0.25±0.05 ≤2.0 0.45±0.10 200 2.1~3.6
Φ5.0 5.5±0.4 0.25±0.05 ≤2.5 0.55±0.10 100 2.6~4.5
Φ6.0 6.5±0.4 0.28±0.05 ≤3.0 0.55±0.10 100 3.1~5.4
Φ8.0 8.5±0.5 0.28±0.05 ≤4.0 0.60±0.10 100 4.2~7.2
Φ10 10.5±0.5 0.30±0.08 ≤5.0 0.60±0.10 100 5.2~9
Φ12 12.5±0.5 0.30±0.08 ≤6.0 0.60±0.10 100 6.2~11
Φ14 14.5±0.5 0.30±0.10 ≤7.0 0.65±0.10 100 7.3~13
Less than the φ 4 φ 14 or greater than for the non-normal casing, order request.

Product introduction:
Magnetic heat-shrinkable sleeve is made of high quality polymers, scientific formula, mechanical blending of polymer alloys, after forming the electron Accelerator irradiation cross-linking and continuous expansion. Products not only with conventional heat-shrinkable sleeve protection, insulation, identifying properties and good electromagnetic compatibility, can greatly improve the electronic components and magnetic properties and stability. Low cost, stable performance, simple installation, contract evenly, can be widely used in the electronic components industry.

Operation indicator
1、Applicable temperature range:-55℃— 125℃; 
2、Shrink temperature:100℃—125℃;
Conformance to standard:Approvals
Conform width ROHS

Test project Test standard Property
Before the materials aging Tensile strength(MPa)
Elongation at break
GB/T1410
GB/T1410
≥10.4
≥200%
Aging conditions
UL224(158°CX 168hr)
Tensile strength(MPa)
Elongation at break
GB/T1410
GB/T1410
≥7.3
≥100%
Concentricity rate    UL224 ≥70%
Heat shock   1MIL-DTL-23053/5C(225℃×4hr) Not tacky,No crack
Cold Blend   UL224(-30℃×1hr) No crack
Density(g/cm3)   ---- ≤2.5
Water absorption   ASTM D570 ≤0.5%
Chemical characteristic Copper stability
Corrosion resistance
UL224(158℃×168hr)
UL224(158℃×168hr)
pass
pass
Environmental performance   RoHS pass
Electrical characteristics
 
Copper volume resistivity
(Ωcm)
Corrosion resistance
Working frequency
Rising range of inductance
GB/T1410
UL224
----
----
≥1×1012
1500v,1min No breakdown 1k-500KHz
≥10%