Product introduction:
By cross-linked polyolefin PE and EVA hot-melt Adhesive extrusion made, the outer layer of polyolefin insulated fire retardant materials, the inner layer of hot-melt glue can buffer the mechanical strain and sealing strong, pursuant to military production. Suitable for all kinds of wire harness, marine wire and cable, and metal pipes need to be sealed, waterproof, moisture-proof, corrosion-resistant applications.

Product features:
Meets military standards ASM-DTL-23053/4 ,Meet the ROHS
Outer flame retardant, UV-resistant
High rate of contraction: 3:1, 4:1
Waterproof, moisture-proof, corrosion-proof and leakage
     
Operation indicator:
Shrink temperature:70℃
End temperature:125℃
Working temperature:-45℃~135℃
Conformance to standard:Approvals,UL224 ,135℃, 600V 

Nominal Size As supplied
(mm)
After recovered( mm ) Standard Packing
(M/Roll)
Metric inch Inside diameter Inside diameter Wall Total  thickness
 
 Adhesivel thickness
HUS-R-3X
¢ 3.2 1/8 ≧3.2 ≦1.00 0.95 ± 0.15 0.35 ± 0.10 200
¢ 4.8 3/16 ≧4.8 ≦1.60 1.10 ± 0.15 0.40 ± 0.10 100
¢ 6.4 1/4 ≧6.4 ≦2.20 1.20 ± 0.15 0.45 ± 0.12 100
¢ 7.9 5/16 ≧7.9 ≦2.70 1.30 ± 0.15 0.50 ± 0.12 100
¢ 9.5 3/8 ≧9.5 ≦3.20 1.40 ± 0.15 0.50 ± 0.12 50
¢ 12.7 1/2 ≧12.7 ≦4.20 1.70 ± 0.15 0.50 ± 0.12 1.22
¢ 15.0 5/8 ≧15.0 ≦5.20 1.80 ± 0.15 0.55 ± 0.15 1.22
¢ 19.1 3/4 ≧19.1 ≦6.30 1.95 ± 0.15 0.55 ± 0.15 1.22
¢ 25.4 1 ≧25.4 ≦8.50 2.05 ± 0.20 0.55 ± 0.15 1.22
¢ 30.0 1-1/4 ≧30.0 ≦10.20 2.20 ± 0.20 0.60 ± 0.15 1.22
¢ 39.0 1-1/2 ≧39.0 ≦13.50 2.50 ± 0.20 0.60 ± 0.15 1.22
¢ 50.0 2 ≧50.0 ≦17.00 2.80 ± 0.25 0.70 ± 0.15 1.22
HUS-R-4X
¢ 4.0 2/13 ≧4.0 ≦1.0 1.05 ± 0.30 0.50 ± 0.20 200
¢ 6.0 1/4 ≧6.0 ≦1.5 1.15 ± 0.30 0.50 ± 0.20 100
¢ 8.0 5/16 ≧8.0 ≦2.0 1.55 ± 0.30 0.60 ± 0.25 100
¢ 12.0 1/2 ≧12.0 ≦3.0 1.75 ± 0.30 0.60 ± 0.25 1.22
¢ 16.0 5/8 ≧16.0 ≦4.0 2.00 ± 0.35 0.70 ± 0.30 1.22
¢ 20.0 15/19 ≧20.0 ≦5.0 2.30 ± 0.40 0.70 ± 0.30 1.22
¢ 24.0 1 ≧24.0 ≦6.0 2.60 ± 0.40 0.75 ± 0.30 1.22
¢ 32.0 1-1/4 ≧32.0 ≦8.0 3.00 ± 0.50 0.90 ± 0.30 1.22
¢ 52.0 2 ≧52.0 ≦13.0 3.35 ± 0.50 0.95 ± 0.30 1.22

Standard colour: black, other colours can be customized.
Specifies the size, cropping can be provided according to the special requirements of the customer  

Product introduction:
By cross-linked polyolefin PE and EVA hot-melt Adhesive extrusion made, the outer layer of polyolefin insulated fire retardant materials, the inner layer of hot-melt glue can buffer the mechanical strain and sealing strong, pursuant to military production. Suitable for all kinds of wire harness, marine wire and cable, and metal pipes need to be sealed, waterproof, moisture-proof, corrosion-resistant applications.

Product features:
Meets military standards ASM-DTL-23053/4 ,Meet the ROHS
Outer flame retardant, UV-resistant
High rate of contraction: 3:1, 4:1
Waterproof, moisture-proof, corrosion-proof and leakage
     
Operation indicator:
Shrink temperature:70℃
End temperature:125℃
Working temperature:-45℃~135℃
Conformance to standard:Approvals,UL224 ,135℃, 600V 

Product Property Test method Test Date
Longitudinal shrinkage ASTM D 2671 -8%~+8%
Tensile strength ASTM D 2671 ≧10.5MPa
Elongation at break ASTM D 2671 ≧300%
Tensile strength after aging 175℃,168hrs ≧8.5MPa
Elongation after aging ≧100%
Heat shock ASTM D 2671
250℃,4hrs
PASS
Cold bend (-30℃, 1hrs) ASTM D 2671
-45℃,4 hrs
No break
Breakdown strength IEC 60243 ≧15KV/mm
Corrosion ASTM D 2671 Pass
Flammability AMS-DTL-2305/5 Self-extinguishing within 30s
Volume resistance IEC 60093 ≧1014Ω․cm(min.)
Hot melt adhesive technology index
water absorption 95 ± 5℃ ASTM E 28
Softening point < 0.5% ASTM D 570
peel strength (PE) ≧120N/25mm ASTM D 1000
peel strength (AI) ≧80N/25mm ASTM D 1000