• Product name: HJM-FR flame-retardant adhesive middle-wall heat shrinkable sleeving

Product introduction:
Flame retardant semi-rigid polyolefin insulation material PE and EVA hot-melt adhesive layer made of good insulation, sealing protection, resistance to impact and wear-resistant, moisture-proof nature, should be used in low-voltage power cable terminals, intermediate connections, marine vessels, marine cable and all kinds of sealing and insulation of the bus and other corrosion, moisture, mechanical seals working environment.

Product features:
Shrink ratio: 3:1, outer flame retardant
Resistance to ultraviolet radiation, moisture-proof, waterproof, strong sealing
Effective electrical insulation protection, excellent mechanical protection properties
Standard colors: black, Red

Operation indicator:
Shrink temperature:70℃
End temperature:125℃
Working temperature:-45℃~125℃
Conformance to standard:Approvals
Meet the ROHS environmental protection, 125 

Product Number/Size
 
Assupplied After recovered (mm) Stand length
M/PCS 
Inside diameter(min) Inside diameter( max)  Outer Wall
Thickness
Adhesive
Thickness 
Total
Thickness 
HJM-FR 10.2/32 ≧10.2 ≦3.0 1.4± 0.20 0.35± 0.10 1.75± 0.25 1.22
HJM-FR 16/5 ≧16.0 ≦5.0 1.5± 0.20 0.40± 0.10 1.90± 0.25 1.22
HJM-FR 19.1/5.6 ≧19.1 ≦5.6 2.0 ± 0.20 0.45± 0.10 2.45± 0.25 1.22
HJM0-FR 25/8 ≧25.0 ≦8.0 2.0 ± 0.20 0.45± 0.10 2.45± 0.25 1.22
HJM-FR 28/9 ≧28.0 ≦9.0 2.0 ± 0.20 0.50± 0.10 2.60± 0.25 1.22
HJM-FR 35/10.2 ≧35.0 ≦10.2 2.2± 0.20 0.78± 0.10 2.70± 0.25 1.22
HJM-FR 38.1/12 ≧38.1 ≦12.0 2.2± 0.20 0.50± 0.10 2.70± 0.25 1.22
HJM-FR 43.2/12.7 ≧43.2 ≦12.7 2.2± 0.20 0.50± 0.10 2.70± 0.25 1.22
HJM-FR  55/16 ≧55.0 ≦16.0 2.3± 0.25 0.50± 0.15 2.80± 0.30 1.22
HJM-FR 63/19 ≧63.0 ≦19.0 2.5± 0.25 0.50± 0.15 3.00± 0.30 1.22
HJM-FR 75/22 ≧75.0 ≦22.0 2.6± 0.25 0.50± 0.15 3.00± 0.30 1.22
HJM-FR 85/25 ≧85.0 ≦25.0 2.8± 0.25 0.50± 0.15 3.30± 0.30 1.22
HJM-FR 95/29 ≧95.0 ≦29.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.22
HJM-FR 115/34 ≧115 ≦34.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.22
HJM-FR 140/42 ≧140 ≦42.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.22
HJM-FR 160/48 ≧160 ≦48.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.00
HJM-FR 180/58 ≧180 ≦58.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.00
HJM-FR 200/60 ≧200 ≦60.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.00
HJM-FR 230/69 ≧230 ≦69.0 3.10± 0.30 0.60± 0.20 3.70± 0.35 1.00

Standard colors: black, red, and other colors can be customized
Specifies the size, cropping can be provided according to the special requirements of the customer 

Product introduction:
Flame retardant semi-rigid polyolefin insulation material PE and EVA hot-melt adhesive layer made of good insulation, sealing protection, resistance to impact and wear-resistant, moisture-proof nature, should be used in low-voltage power cable terminals, intermediate connections, marine vessels, marine cable and all kinds of sealing and insulation of the bus and other corrosion, moisture, mechanical seals working environment.
     
Operation indicator:
Shrink temperature:70℃
End temperature:125℃
Working temperature:-45℃~125℃
Conformance to standard:Approvals
Meet the ROHS environmental protection, 125 

Product Property Test method Test Date
Longitudinal shrinkage ASTM D 2671 0~+5%
Tensile strength ASTM D 2671 ≧12MPa
Elongation at break ASTM D 2671 ≧300%
Tensile strength at break after aging 158℃,168hrs ≧9.0MPa
Elongation after aging ≧100%
Breakdown strength IEC 60243 ≧15KV/mm
Corrosion ASTM D 2671 Pass
Flammability AMS-DTL-23053/5 Outer layer Self-extinguishing within 30s
Volume resistance IEC 60093 ≧1014Ω․cm(min.)
Hot melt adhesive technology index
water absorption 95 ± 5℃ ASTM E 28
Softening point < 0.5% ASTM D 570
peel strength (PE) ≧120N/25mm ASTM D 1000
peel strength (AI) ≧80N/25mm ASTM D 1000