JZT- Motor Insulation Tube (striped Mylar Tube)


Product Overview:

JZT- Polyester Tube ( Mylar tube ) Mainly used in welding spot, joint, coil, transformer, motor, wire, heating element, capacitor, telephone relay, temperature controller, electronic equipment, household appliance wire harness, automobile wire harness, wire and cable, metal pipe and other temperature insulation and mechanical protection.  
Contact us
  • Product Features
  • Specifications
  • Technical data
  • Video
  • JZT- Polyester Tube ( Mylar tube ) are made of dupont MO materials, Environmental protection.

    Key words:
    • Mylar tube
    • Polyester Tube
    • Motor protection sleeving
    • Motor insulation tube
  • JZT- Polyester sleeve  ( Mylar tube )

    Specification  

    Inside diameter0.026 inch2 inch0.66mm50.8mm

    Length0.62 inch48 inch57mm1219mm 

    Wall Thickness0.001 inch0.03 inch0.0254mm0.76mm 

     

     

    ColorTransparentcolorstripe

     

    Ps: The inner diameter is less than 1.0, the production process is different,

    the thickness can only be 0.03, and the thickness of 1.0 or more can be customized.

         The inner diameter is 1.2-2.0 (thickness 0.05-0.1),

    ID 2.0 (thickness 0.05-0.025) can be customized.

  • Variety Capability

    VarietyCapability

    Polyester

    Low Shrinkable Polyester

    Heat Shrinkable Polyester

    shrinkable rateradical

    2

    8-12

    32

    shrinkable rateportrait

    2

    8-12

    35

    working temperature

    -60℃-150℃

    melting temperature

    250℃-255℃

    voltage to strike through

    25℃ ( 50cycle))
    2650v ,0.0254mm/min

     

    125℃( 50cycle

    2125V, 0.0254mm/min

    flammability

    spontaneous quench

    resistance

    The conductor is resistant to acid and alkali corrosion, impregnation, mildew, corona discharge, industrial solvent, external mechanical damage, oil and special liquid

    sopping capacity

    Maximum absorption is 75% after 24 hours immersion

    toluene extraction

    2