Product Overview:

Flame retardant polyolefin PE and flame retardant EVA hot-melt Adhesive extrusion made according to military production. Can buffer the mechanical strain and sealing strong, applicable to all types of wire harnesses, marine wire and cable, and metal pipes need to be sealed, waterproof, moisture-proof, corrosion-resistant environment.
Contact us
  • Product Features
  • Specifications
  • Technical data
  • Video
  • Operation indicator:
    Shrink temperature: 70℃
    End temperature: 125℃
    Working temperature: -45℃ ~ 135℃
     

    Conformance to standard:Meet UL224 ,135℃,  600V 

    Meet military standard ASM-DTL-23053/4.
    High flame retardant  ( within the outer PE, EVA meets flame retardant)
    High rate of contraction:   3:1,    4:1
    Waterproof, moisture-proof, corrosion-resistant, leak-proof, UV-resistant, Comply with the ROHS2.0

    Key words:
    • Heat Shrink tube with adhesive
    • Heat shrinkable tubing with glue
    • Waterproof heat shrink tube
  • Nominal Size As supplied(mm) After recovered ( mm ) Standard 
    Packing

     (M/Roll)
    (mm) (inch) D(min.)       d(min.)  WT:  t.
    Inside diameter Inside diameter Wall Total Thickness  Adhesive thickness
    HUS-GR-3X
    ¢ 3.2 1/8 ≥3.2 ≤1.00 0.95 ± 0.15 0.35 ± 0.10 200
    ¢ 4.8 3/16  ≥4.8 ≤1.60 1.10 ± 0.15 0.40 ± 0.10 100
    ¢ 6.4 1/4 ≥6.4 ≤2.20 1.20 ± 0.15 0.45 ± 0.12 100
    ¢ 7.9 5/16 ≥7.9 ≤2.70 1.30 ± 0.15 0.50 ± 0.12 100
    ¢ 9.5 3/8 ≥9.5 ≤3.20 1.40 ± 0.15 0.50 ± 0.12 50
    ¢ 12.7 1/2 ≥12.7 ≤4.20 1.70 ± 0.15 0.50 ± 0.12 1.22
    ¢ 15.0 5/8 ≥15.0 ≤5.20 1.80 ± 0.15 0.55 ± 0.15 1.22
    ¢ 19.1 3/4 ≥19.1 ≤6.30 1.95 ± 0.15 0.55 ± 0.15 1.22
    ¢ 25.4 1 ≥25.4 ≤8.50 2.05 ± 0.20 0.55 ± 0.15 1.22
    ¢ 30.0 1-1/4 ≥30.0 ≤10.20 2.20 ± 0.20 0.60 ± 0.15 1.22
    ¢ 39.0 1-1/2 ≥39.0 ≤13.50 2.50 ± 0.20 0.60 ± 0.15 1.22
    ¢ 50.0 2 ≥50.0 ≤17.00 2.80 ± 0.25 0.70 ± 0.15 1.22
    HUS-GR-4X
    ¢ 4.0 2/13 ≥4.0 ≤1.0 1.05 ± 0.30 0.50 ± 0.20 200
    ¢ 6.0 1/4 ≥6.0 ≤1.5 1.15 ± 0.30 0.50 ± 0.20 100
    ¢ 8.0 5/16 ≥8.0 ≤2.0 1.55 ± 0.30 0.60 ± 0.25 100
    ¢ 12.0 1/2 ≥12.0 ≤3.0 1.75 ± 0.30 0.60 ± 0.25 1.22
    ¢ 16.0 5/8 ≥16.0 ≤4.0 2.00 ± 0.35 0.70 ± 0.30 1.22
    ¢ 20.0 15/19 ≥20.0 ≤5.0 2.30 ± 0.40 0.70 ± 0.30 1.22
    ¢ 24.0 1 ≥24.0 ≤6.0 2.60 ± 0.40 0.75 ± 0.30 1.22
    ¢ 32.0 1-1/4 ≥32.0 ≤8.0 3.00 ± 0.50 0.90 ± 0.30 1.22
    ¢ 52.0 2 ≥52.0 ≤13.0 3.35 ± 0.50 0.95 ± 0.30 1.22

    Standard colour: black, other colours can be customized .
    Specifies the size, cropping can be provided according to the special requirements of the customer .

  • Product Properties Test method Test Date
    Longitudinal shrink ratio ASTM D 2671 -8%~+8%
    Tensile strength ASTM D 2671 ≥12.2MPa
    Elongation at break ASTM D 2671 ≥300%
    Tensile strength after aging 175℃,168hrs ≥8.5MPa
    Elongation after aging ≥100%
    Heat shock ASTM D 2671 
    250,4hrs
    PASS
    Cold bend (-30℃, 1hrs) ASTM D 2671 
    -45,4 hrs
    No break
    Breakdown strength IEC 60243 ≥15KV/mm
    Corrosion ASTM D 2671 Pass
    Flammability AMS-DTL-2305/5 Self-extinguish in 30 seconds
    Volume resistance IEC 60093 ≥1014Ω.cm(min.)
    Hot melt adhesive technology index
    water absorption 95 ± 5℃ ASTM E 28
    Softening point < 0.5% ASTM D 570
    peel strength (PE) ≥120N/25mm ASTM D 1000
    peel strength (AI) ≥80N/25mm ASTM D 1000