Curved Heat Shrink Molded Shapes
Product Overview：
- Product Features
- Specifications
- Technical data
- Video
-
Product Model :
KY/MS-2A/C-01
Application :
This right angle Heat shrink Molded Shapes(Boots) provides mechanical protection and stress relief. The sleeve has no lip so it can be heat shrunk directly onto the threads of the attachment.
-
KY/MS-2A/C-01~09 ：
NO.
Model
Dimensions
before heat shrink
(mm)
Dimensions After heat shrink(mm)
Hmin
Jmin
Hmax
Jmax
W±20％
P±10％
-4,-25,-71
-100
-12
1
KY/MS-2A/C-01
17.8
17.8
10.9
9.9
7.9
3.8
1.02
17.3
2
KY/MS-2A/C-02
24.9
24.9
16.0
18.0
10.2
5.3
1.27
21.3
3
KY/MS-2A/C-03
30.0
30.0
21.1
20.6
14.2
6.4
1.52
26.9
4
KY/MS-2A/C-04
32.5
32.5
22.9
22.9
17.3
6.9
1.78
36.6
5
KY/MS-2A/C-05
36.1
36.1
27.4
26.4
21.8
8.4
1.78
43.7
6
KY/MS-2A/C-06
43.9
43.9
28.4
27.4
27.4
9.4
2.03
53.6
7
KY/MS-2A/C-07
53.1
53.1
48.3
46.7
33.8
15.0
3.30
75.7
8
KY/MS-2A/C-08
67.6
67.6
58.4
54.4
44.2
20.3
3.81
97.5
9
KY/MS-2A/C-09
87.6
87.6
68.8
63.0
55.4
23.4
4.57
128.0
-
Heat Shrink Molded Shapes Material Properties
Material code
Material category
Hardness (Shore A)
Operating temperature
installation temperature
Material properties
-4
Mildew resistant soft flame retardant polyolefin
82±2
﹣55～135℃
150℃
Mildew-resistant, especially soft, flame-retardant, abrasion-resistant, liquid-resistant
-12
Modified fluororubber
87±2
﹣55～200℃
220℃
Soft, flame retardant, heat resistant, excellent oil and solution resistance
-25
Solution resistant rubber
92±2
﹣55～150℃
175℃
Semi-hard, flame-retardant, chemical-resistant, abrasion-resistant, liquid-resistant, heat-resistant
-71
Semi-hard modified polyolefin
90±2
﹣55～135℃
150℃
Semi-hard, flame-retardant, liquid-resistant, heat-resistant, wear-resistant
-100
Halogen Free Flame Retardant Polyolefin
90±2
﹣30～120℃
150℃
Halogen free, flame retardant, low smoke, environmentally friendly
Heat Shrink Molded Shapes performance index
performance
Test items
Unit
Material code
experiment method
-4
-12
-25
-71
-100
physical
properties
Size Appearance After Shrinking
/
No cracks, the product conforms to the model size after shrinkage
JB/T7829-2006
Hardness (Shore)
degree
82±2
87±2
92±2
90±2
90±2
GB/T2411-2008
tensile strength
Mpa
≥16
≥12
≥14
≥14
≥10
GB/T1040.2-2006
Elongation at break
﹪
≥450
≥350
≥350
≥300
≥250
GB/T1040.2-2006
water absorption
(23℃ 24h)
％
≤0.15
≤0.15
≤0.15
≤0.15
≤0.15
GB/T2951.13-2008
density
g/c㎥
1.1±0.1
1.0±0.1
1.1±0.1
1.2±0.1
1.3±0.1
GB/T1033-2008
low temperature embrittlement
﹣55±5℃ 4h
℃
No cracking, no flowing,
/
GB/T5470-2008
Aging
performance
Oven / Heat Aging 135℃ 168h
Elongation at break
﹪
≥350
/
/
≥200
≥100
GB/T7141-2008
tensile strength
Mpa
≥12
/
/
≥10
≥8
GB/T7141-2008
Oven / Heat Aging 150℃ 168h
Elongation at break
﹪
/
/
≥250
/
/
GB/T7141-2008
tensile strength
Mpa
/
/
≥10
/
/
GB/T7141-2008
Oven / Heat Aging 200℃ 168h
Elongation at break
﹪
/
≥250
/
/
/
GB/T7141-2008
tensile strength
Mpa
/
≥10
/
/
/
GB/T7141-2008
Thermal shock 200℃ 4h
/
No crack, no flowing, no dripping
JB/T7829-2006
Thermal shock 300℃ 4h
/
/
No crack,
/
/
/
JB/T7829-2006
Electrical
properties
Dielectric strength
Kv/mm
≥14
≥10
≥10
≥12
≥10
GB/T1408.1-2016
Volume resistivity
Ω.cm
≥1×1011
≥1×1010
≥1×1010
≥1×1010
≥1×1010
GB/T1410-2006
Chemical
properties
flame retardancy
/
V-1
GB/2408-2008
Copper corrosion
/
150±5℃ 168h pass
UL224
smoke density
/
/
/
/
/
≤32
GB/T8323.2-2008
Mold resistance
/
≤2
≤2
≤2
≤2
/
GJB150.10A-2009
Damp heat properties
humidity95％ 60℃～30℃ transform5次，24h.
Qualified cycle test
GJB150.9A-2009
Salt spray performance
5% salt solution, continuous spraying at 35°C
for 48h, Good appearance, no corrosion
GJB150.11A-2009
Media resistance
aviation oil
F40 （23℃ 24h）
Tensile Strength
Mpa
10.5
9
11
8
6
GB/T2951.21-2008
Elongation at break
％
350
230
300
200
180
GB/T2951.21-2008
lubricating oil 23℃ 24h
Tensile Strength
Mpa
≥12
≥10
≥12.5
≥9
≥7
GB/T2951.21-2008
Elongation at break
％
380
260
330
220
200
GB/T2951.21-2008