T-Style Heat Shrink Molded Boots


Product Overview:

T-Style Heat Shrink Molded Shapes Cable splits and transitions provide strain relief, sealing and mechanical protection for cable assemblies, cable splits and transitions used in harsh environments
Contact us
  • Product Features
  • Specifications
  • Technical data
  • Video
  • Product Model :    KY/MS-3A/T-01



     

    Application :  This thin cable uses T-shaped split Heat shrink Molded Shapes(Boots) to provide mechanical protection and strain relief at the cable splits.

    KY/MS-3B/T1-01

     

    Application:

    This T-Heat shrink Molded Shapes(Boots) provides mechanical protection and strain relief at the cable splits.

     

  • KY/MS-3A/T-01~04

     

    NO.

    Model

    Dimensions

    before heat shrink

    (mm)

    Dimensions After heat shrink(mm)

    Hmin

    Jmin

    Kmin

    Hmax

    Jmax

    Kmax

    W±30%

    P±10%

    1

    KY/MS-3A/T-01

    19.8

    13.2

    13.2

    6.6

    6.6

    6.6

    1.02

    80.8

    2

    KY/MS-3A/T-02

    34.3

    22.9

    22.9

    11.4

    11.4

    11.4

    1.27

    120.4

    3

    KY/MS-3A/T-03

    60.2

    40.1

    40.1

    20.1

    20.1

    20.1

    1.52

    175.8

    4

    KY/MS-3A/T-04

    83.3

    54.9

    54.9

    33.3

    33.3

    33.3

    1.78

    242.3

    KY/MS-3B/T1-01~05 

    NO.

    Model

    Dimensions

    before heat shrink

    (mm)

    Dimensions After heat shrink(mm)

    Hmin

    Jmin

    Kmin

    Hmax

    Jmax

    Kmax

    HW&W±20%

    JW±20%

    P±10%

    1

    KY/MS-3B/T1-01

    13.2

    13.2

    6.6

    5.8

    5.8

    3.0

    1.52

    1.02

    52.3

    2

    KY/MS-3B/T1-02

    26.9

    26.9

    6.6

    12.4

    12.4

    3.0

    2.54

    1.02

    83.3

    3

    KY/MS-3B/T1-03

    26.9

    26.9

    13.2

    12.7

    12.7

    5.8

    2.54

    1.52

    107.7

    4

    KY/MS-3B/T1-04

    55.6

    55.6

    13.2

    25.4

    25.4

    5.8

    4.57

    1.52

    180.6

    5

    KY/MS-3B/T1-05

    55.6

    55.6

    26.9

    25.4

    25.4

    12.4

    4.57

    2.54

    222.3

     

     

  • Heat Shrink Molded Shapes Material Properties

     

     

    Material code

    Material category

    Hardness (Shore A)

    Operating temperature

    installation temperature

    Material properties

    -4

    Mildew resistant soft flame retardant polyolefin

    82±2

    55~135℃

    150℃

    Mildew-resistant, especially soft, flame-retardant, abrasion-resistant, liquid-resistant

    -12

    Modified fluororubber

    87±2

    55~200℃

    220℃

    Soft, flame retardant, heat resistant, excellent oil and solution resistance

    -25

    Solution resistant rubber

    92±2

    55~150℃

    175℃

    Semi-hard, flame-retardant, chemical-resistant, abrasion-resistant, liquid-resistant, heat-resistant

    -71

    Semi-hard modified polyolefin

    90±2

    55~135℃

    150℃

    Semi-hard, flame-retardant, liquid-resistant, heat-resistant, wear-resistant

    -100

    Halogen Free Flame Retardant Polyolefin

    90±2

    30~120℃

    150℃

    Halogen free, flame retardant, low smoke, environmentally friendly

     

     

     

    Die shrink sleeve material performance index

     

    performance

    Test items

    Unit

    Material code

    experiment method

    -4

    -12

    -25

    -71

    -100

    physical

     

    properties

     

    Size Appearance After Shrinking

    /

    No cracks, the product conforms to the model size after shrinkage

    JB/T7829-2006

     

    Hardness (Shore)

    degree

    82±2

    87±2

    92±2

    90±2

    90±2

    GB/T2411-2008

     

    tensile strength

    Mpa

    ≥16

    ≥12

    ≥14

    ≥14

    ≥10

    GB/T1040.2-2006

     

    Elongation at break

    ≥450

    ≥350

    ≥350

    ≥300

    ≥250

    GB/T1040.2-2006

     

    water absorption

    (23℃ 24h)

    ≤0.15

    ≤0.15

    ≤0.15

    ≤0.15

    ≤0.15

    GB/T2951.13-2008

     

    density

    g/c

    1.1±0.1

    1.0±0.1

    1.1±0.1

    1.2±0.1

    1.3±0.1

    GB/T1033-2008

    low temperature embrittlement

    55±5℃  4h

    No cracking, no flowing,

    /

    GB/T5470-2008

    Aging  

     performance

    Oven / Heat Aging     135℃ 168h

    Elongation at break

    ≥350

    /

    /

    ≥200

    ≥100

    GB/T7141-2008

    tensile strength

    Mpa

    ≥12

    /

    /

    ≥10

    ≥8

    GB/T7141-2008

    Oven / Heat Aging       150℃  168h

    Elongation at break

    /

    /

    ≥250

    /

    /

    GB/T7141-2008

    tensile strength

    Mpa

    /

    /

    ≥10

    /

    /

    GB/T7141-2008

    Oven / Heat Aging       200℃  168h

    Elongation at break

    /

    ≥250

    /

    /

    /

    GB/T7141-2008

    tensile strength

    Mpa

    /

    ≥10

    /

    /

    /

    GB/T7141-2008

    Thermal shock 200℃ 4h

    /

    No crack, no flowing, no dripping

    JB/T7829-2006

    Thermal shock 300℃ 4h

    /

    /

    No crack,

    /

    /

    /

    JB/T7829-2006

    Electrical

    properties

    Dielectric strength

    Kv/mm

    ≥14

    ≥10

    ≥10

    ≥12

    ≥10

    GB/T1408.1-2016

    Volume resistivity

    Ω.cm

    1011

    1010

    1010

    1010

    1010

    GB/T1410-2006

    Chemical

     properties

    flame retardancy

    /

    V-1

    GB/2408-2008

    Copper corrosion

    /

    150±5℃  168h  pass

    UL224

    smoke density

    /

    /

    /

    /

    /

    ≤32

    GB/T8323.2-2008

    Mold resistance

    /

    ≤2

    ≤2

    ≤2

    ≤2

    /

    GJB150.10A-2009

    Damp heat properties

    humidity95% 60℃~30℃ transform5次,24h.

    Qualified cycle test

    GJB150.9A-2009

    Salt spray performance

    5% salt solution, continuous spraying at 35°C

    for 48h, Good appearance, no corrosion

    GJB150.11A-2009

    Media resistance

    aviation oil 

    F40        (23℃ 24h)

    Tensile Strength

    Mpa

    10.5

    9

    11

    8

    6

    GB/T2951.21-2008

    Elongation at break

    350

    230

    300

    200

    180

    GB/T2951.21-2008

    lubricating oil            23℃ 24h

    Tensile Strength

    Mpa

    ≥12

    ≥10

    ≥12.5

    ≥9

    ≥7

    GB/T2951.21-2008

    Elongation at break

    380

    260

    330

    220

    200

    GB/T2951.21-2008